1、LG POE基本物性表 Joseph ZhouSungShinChina 2012物性指标 实验方法 单位 LC100 LC170 LC180 LC670 LC565 LC175Melt Index 熔融指数（ 2.16kg,190)ASTM D 1238 g/10min 1.2 1.1 1.2 5.0 5.0 1.1Density 密度 ASTM D 1505 g/cm3 0.903 0.870 0.885 0.870 0.865 0.870Mooney Viscosity ML1+4121ASTM D 1646 MU 23 23 20 9 8 22Tensile Strength Brea
2、k断裂强度 MPa 24.5 9.5 17.5 5.5 1.8 5.1Elongation Break断裂伸长ASTM D 638% 660 900 670 1000 550 980Flexural Modulus, 1%撓曲模数ASTM D 790 Mpa 83 14 30 13 7.8 16Hardness 表面硬度 ASTMD2240 ShoreA 88 71 82 70 54 70Tear Strength, Type C 撕裂強度ASTM D 624 kN/m 87 40 58 38 20 38Melting Point, DSC融点 LG METHOD 0C 96 58 73 58 36 52Glass Transition Temperature玻璃轉化温度 LG METHOD0C -31 -53 -45 -55 -54 -53