1、PBT, 30 % glass fibres, injection moulding, flame retardantISO Shortname: ISO 7792-1-PBT,GFHMR,09-110,GF30; ISO 1043-PBT GF FR(17)Property Test Condition Unit Standard guide valueRheological propertiesCMelt volume-flow rate 260 C; 5 kg cm/(10 min) ISO 1133-1 37CMolding shrinkage, parallel 60x60x2; 2
2、50 C / WZ 80C; 600 bar% ISO 294-4 0.3CMolding shrinkage, transverse 60x60x2; 250 C / WZ 80C; 600 bar% ISO 294-4 0.9Post- shrinkage, parallel 60x60x2; 120 C; 4 h % ISO 294-4 0.1Post- shrinkage, transverse 60x60x2; 120 C; 4 h % ISO 294-4 0.1Mechanical properties (23 C/50 % r. h.)CTensile modulus 1 mm/
3、min MPa ISO 527-1,-2 11500CTensile Stress at break 5 mm/min MPa ISO 527-1,-2 125CTensile Strain at break 5 mm/min % ISO 527-1,-2 2.1CCharpy impact strength 23 C kJ/m ISO 179-1eU 50CCharpy impact strength -30 C kJ/m ISO 179-1eU 50CCharpy notched impact strength 23 C kJ/m ISO 179-1eA 10CCharpy notched
4、 impact strength -30 C kJ/m ISO 179-1eA 10Izod impact strength 23 C kJ/m ISO 180-1U 45Izod impact strength -30 C kJ/m ISO 180-1U 45Izod notched impact strength 23 C kJ/m ISO 180-1A 10Izod notched impact strength -30 C kJ/m ISO 180-1A 10Flexural modulus 2 mm/min MPa ISO 178-A 10500Flexural strength 2
5、 mm/min MPa ISO 178-A 200Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.6Ball indentation hardness N/mm ISO 2039-1 186CPuncture energy 23 C J ISO 6603-2 2.3CPuncture energy -30 C J ISO 6603-2 2.1CPuncture maximum force 23 C N ISO 6603-2 669CPuncture maximum force -30 C N ISO 6603-2 649T
6、hermal propertiesCMelting temperature 10 C/min C ISO 11357-1,-3 225CTemperature of deflection under load 1.80 MPa C ISO 75-1,-2 200CTemperature of deflection under load 0.45 MPa C ISO 75-1,-2 220Vicat softening temperature 50 N; 120 C/h C ISO 306 205CCoefficient of linear thermal expansion, parallel
7、 23 to 55 C 10-4/K ISO 11359-1,-2 0.2CCoefficient of linear thermal expansion, transverse 23 to 55 C 10-4/K ISO 11359-1,-2 0.9CBurning behavior UL 94 0.38 mm Class UL 94 V-0CBurning behavior UL 94 0.8 mm Class UL 94 V-0COxygen index Method A % ISO 4589-2 32Pocan B 4239 000000Page 1 of 3Edition 18.07
8、.2013Property Test Condition Unit Standard guide valueThermal conductivity 23 C W/(mK) ISO 8302 0.24Resistance to heat (ball pressure test) C IEC 60695-10-2 213Temperature index (Tensile strength) 20000 h C IEC 60216-1 155Halving interval (Tensile strength) C IEC 60216-1 9.3Relative temperature inde
9、x (Tensile strength) C UL 746B 140Temperature index (Tensile impact strength) 20000 h C IEC 60216-1 130Halving interval (Tensile impact strength) C IEC 60216-1 8.4Relative temperature index (Tensile impact strength) C UL 746B 110Temperature index (Electric strength) 20000 h C IEC 60216-1 145Halving
10、interval (Electric strength) C IEC 60216-1 12Relative temperature index (Electric strength) C UL 746B 125Glow wire test (GWFI) 0.8 mm C IEC 60695-2-12 960Glow wire test (GWIT) 0.8 mm C IEC 60695-2-13 725Glow wire test (GWIT) 1.6 mm C IEC 60695-2-13 725Glow wire test (GWIT) 3.0 mm C IEC 60695-2-13 72
11、5Electrical properties (23 C/50 % r. h.)CRelative permittivity 100 Hz - IEC 60250 3.9CRelative permittivity 1 MHz - IEC 60250 3.8CElectric strength 1 mm kV/mm IEC 60243-1 35CComparative tracking index CTI Solution A V IEC 60112 275Electrolytic corrosion Rating IEC 60426 A/B 1Other properties (23 C)C
12、Density kg/m ISO 1183 1670Bulk density kg/m ISO 60 800Processing conditions for test specimensCInjection molding-Melt temperature C ISO 294 250CInjection molding-Mold temperature C ISO 294 80Processing recommendationsDrying time circulating air dryer h - 4-8Drying temperature circulating air dryer C
13、 - 120Residual moisture content % Acc. to KarlFischer0-0.02Melt temperature (Tmin - Tmax) C - 240-260Mold temperature C - 80-100CThese property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data forplastics according to ISO 10350.P
14、ocan B 4239 000000Page 2 of 3Edition 18.07.2013DisclaimerDisclaimer for sales productsThis information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies whereproprietary rights of third parties are involved
15、. Our advice does not release you from the obligation to verify the information currently provided - especially that containedin our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use andprocessing
16、 of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your ownresponsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.Test valuesUnless specified t
17、o the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guidevalues only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the
18、design of themould/die, the processing conditions and the coloring.Processing noteUnder the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health andwell-being of the machine operatives, tolerance limits for
19、 the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at theworkplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products,the prescribed processing
20、 temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects inthe heating system, special care and controls are essential in these areas.LANXESS DEUTSCHLAND GMBH | D - 51369 LEVERKUSEN LANXESS Deutschland GmbHPocan B 4239 000000Page 3 of 3Edition 18.07.2013