1、Project application of the high-performance concrete of fly ashThe summary Every performance of this text to high-performance concrete of fly ash has done detailed research, and to the concrete respectively to person who mix of fly ash Kinds of influence of performance and fly ash concrete some ques
2、tions that should notice carry on analysis and discussion in not constructing. 1. SummaryFly ash, as a kind of industrial waste material, resources are abundant , cheap, and contain a large amount of active composition , it is modern concrete Central Africa A often important component part . The hig
3、h-quality fly ash is applied to the concrete rationally , not only can replace the cement partly , save the fabrication cost of the project, And, its peculiar performance can be used in the concrete of various kinds of instructions for use very effectively, improve the performance of the concrete, I
4、t is the ideal in the high-performance concrete that admixes the material . Among it is at concrete not modern, whose name is already with cement in fly ash, collect material , water , admixture and Kind is important, become a component part in concrete. Fly ash high-performance concrete regard dura
5、bility as main goal go on design mix Congeal the soil . It regards excellent durability (instead of the high strength) as the main characteristic , that is to say, concrete capital of any grade of intensity Can make into the high durability concrete . In order to reach high durability, the performan
6、ce that the fly ash concrete should possess is: Mixing the state newly well Work,namely, without emanating, secreting by water, so that shaping the even , closely knit by mobility, harden not shrinking subsiding early water and Water shrink light, warm to rise low, harden course is it dwindle to do,
7、 in order to reach having the initial crack, the permeability after hardenning is low. 2 “ function “ and “ effect “ of the fly ash are fly ash material technology and application foundation of the project. Mix and add the powder of the concrete Coal ash, in conformity with understanding that the fu
8、nction of the fly ash is made overallly, by “ volcanic ash react “ and “ economic component part“ general to fly ash originally Read , expand technological consciousness of “ fly ash effect “ to , make fly ash function can serve performance of concrete improve with quality raising better. The role i
9、n concrete of fly ash has the following several points: (1) . Shape effect: It is spongy vitreous body , little pearl of silicate glass of aluminium that the main mineral of the fly ash makes up , smooth the body surface of these spherical glass, the grain size is thin, the quality is pre-pressing,
10、inside smaller than the surface area, the strength of absorbing to water is small, this line of physical characteristics, reduce concrete rub obstruction inside , favorable to improvement , concrete of mobility not merely; And, have “ reducing water “ function in various degree on the concrete; (2)
11、. Active effect: The active composition SiO2 of the fly ash and water result of AI2O3 and cement react in a situation that there is water, producing water silicic acid calcium (C-S-H ) and water sour calcium (C-A-S-H ) of sulphur aluminium, these responses nearly all go on in the grout hole, water t
12、hat produce result pack , cut apart the heavy original hole , make the hole thinning, can reduce the hole rate within the concrete , change the hole structure , improve glueing the function of forming of concrete every component part ; (3) . Collect the material effect a little: Very small particle
13、of fly ash even to is it among cement particle , pack the hole to distribute, play a role in getting to “ thinning hole “ , meanwhile , prevent glueing gathering each other of the cement particle, and make it in state of dispersing , help water of the mixture to react, the fly ash will not be totall
14、y with reacting with water result of the cement, can keep its “ collecting the material effect a little “ for a long time ; (4) . Effect of the interface: It is the weak link in the concrete structure to collect the interface between the material and cement stone, width of transition area as water f
15、or dust than, collect there arent material , transition area have than grout body more, heavy hole. Mixing can reduce the regional width of the transition to add the fly ash , interfere Ca (OH ) orientation of 2 crystal in the transition area, improve the intensity of interface and density in the co
16、ncrete. (5) Performance of the fly ash concrete The change of the fly ash to concrete performance can be divided into three stages: 1 . Mix concrete stage newly: Influence the coagulation time of the concrete , is improving and easy , change rheology nature , can improve pump ,etc.;(6) . The concret
17、e stage while hardenning: Regulate the course of hardenning, reduce the heat of hydration;3 . The concrete stage after hardenning: Raise the intensity on later stage , raise every durability, such as anti-permeability, resist the sulphate corroding, suppress the alkali - Collect the material and rea
18、ct etc3.1 Intensity The fly ash has three kinds of influence on the intensity of concrete: Reduce water consumption , increase glued material content and reflect through the long-term volcanic ash that raises his intensity. The particle in the fly ash of low calcium is the silicon oxygen tetrahedron
19、 structure, ones own activation is very low. In the final result of the cement, high alkaline water silicic acid calcium and crystallization of 2 colloid of Ca (OH ) are very low in intensity, especially Ca (OH) 2 ask vigorous to come 1-2% , stone of intensity only, but Ca (OH) 2 volume account for
20、whole cement 25% , stone of volume. A large number of silicon , aluminium oxide that contain in the fly ash, can and high alkaline water silicic acid calcium 2 responses take place with Ca (OH ) 2 progressively, produce intensity than high low alkaline water silicic acid calcium , so , make cement s
21、tone water glue congeal quantity of material increase, and make its quality improved by a large margin , is favorable to the improvement of the intensity of concrete. Meanwhile, to is it can disperse cement particle to mix fly ash, make cement to be ink sufficient, improve closely knit degree of the
22、 grout , make the intensity of the interfaces of the aggregate and grout in the concrete improve. Fly ash is it draw intensity compare with contribution of the bending strength compression strength to be heavy to confront with each other, this is useful to resisting the performance of splitting of c
23、oncrete. The elastic mould amount of the fly ash concrete is similar to compression strength, it is early and on the low side, improve progressively later stage , get 28d the constant basic concrete is raised by 5-10%. With to hold strength of wrapping up in reinforcing bar, 28d , fly ash of concret
24、e is it form intensity the same with ,etc. basic concrete of grade basically to glue, but homogeneity, fly ash of concrete fine, is it form intensity person who test getting dispersed and kind than basic concrete to glue. Water two times of the fly ash reacts and generally starts after the concrete
25、builds 14d, when temperature is low , will reflect necessary time is longer. If strict with early intensity of the concrete, the mixing amount of the fly ash is unsuitable to exceed 30%, winter construction large volume at the concrete, the mixing amount of the fly ash is unsuitable to exceed 20% no
26、n-. Because modern concrete China and foreign countries add use of pharmaceutical, on one hand, reducible concrete mix and stir water consumption, it reduce by dust water than,of not lasting concrete density of cement; On the other hand, water-reducing agent can make cement silicic acid calcium ink
27、Ca (OH ) produced 2 increase, help fly ash and water two times of 2 of Ca (OH ) to reflect , excites the activation of the fly ash, this effectual for early intensity to improve fly ash, in addition use fly ash activation excite pharmaceutical or in large volume use strong cement early among the con
28、crete non-, can compensate mixing the impact on early intensity of concrete of fly ash too. 3.2 and easy Whether fly ash there are the following several points to concrete and getting easy improvement function. .The high-quality fly ash contains more than 70% of the spherical vitreous bodies, too sm
29、ooth to have raised angle the body surface of these spherical glass, performance is steady, play a kind of lubricated function which is similar to the bearing in the pump sending , shaking the course of smashing of the concrete; .Mix particle apt to gather group cement in the concrete newly, to is i
30、t can disperse cement particle effectively to mix fly ash, release more thick liquid body is it lubricate aggregate to come , help concrete work the improvement of performance ; .Mix fly ash can compensate detailed deficiency of bits in the detailed aggregate , cut off mortar base body secrete conti
31、nuity , water of channel, the fly ash that at the same time quality is good can reduce the mixing water consumption of the concrete under the same consistency, make water dust of concrete than reduce light level to , is it secrete ink and emanate the phenomenon to reduce. 3.3 shrinking The shrink of
32、 the concrete relates to the fact that the mixing water consumption and thick liquid body body of the concrete are accumulated, the less water consumption is, shrink the smaller. High-quality fly ash water requirement than smaller than 100% , mix and stir reduction , water of quantity make mix fly a
33、sh concrete after the 28d since dry to shrink and not dry to shrink little. Fly ash concrete is it is it mix with fly ash improvement of quantity reduce too to contract to do. But because water , fly ash of concrete reponse slowly, moisture evaporate fast, so between fly ash and to do epitome to be
34、loud and very much heavy in early days concrete. For prevent early shrink , fly ash of concrete from fracture , should strengthen in early days raising to it 3.4 creepsIssue in the past will it be age one day, intensity of concrete relatively low, issue is it it meets an emergency to be heavy than o
35、rdinary concrete too to creep corresponding age, but with ordinary concrete fly ash in one age one creep and was smaller than the ordinary concrete after this concrete of intensity. 3.5 carbonization performance Fly ash concrete resist carbonization to be performance relatively poor. Cement consumpt
36、ion , fly ash of concrete reduce, cement water Ca (OH ) 2 too corresponding to reduce quantity that appear, and volcanic ash is it consume Ca (OH ) 2 of a certain amount too to react, make hydrogen ion index of the concrete reduce, will increase the speed of carbonization of the concrete. Unless esp
37、ecially at water in early days, fly ash the low in degree in response in volcanic ash,fly ash- there is the loose in structure in hole in system cement, CO2 , O2 , moisture ,etc. invade obstruction small, so carbonization is relatively large in depth. With the growth of one and gradual full play of
38、the fly ash volcanic ash effect of age, the speed of carbonization will be reduced gradually. Carbonization , fly ash of concrete as water for dust in depth than and fly ash last increase of quantity and not increased to some extent. Than 0.5-0.55 in water dust, fly ash person who mix greater than 3
39、0% and under the general construction situation of competence, the depth of carbonization of the concrete can reach about 20mm in 15-17. Carbonization reacts and goes on within the range of certain relative humidity fastest, otherwise, the response is relatively slow. Under or is close to 100% 25% i
40、n the relative humidity, namely the occasion in the abundant dryness or water saturation of concrete, have more difficult to produce carbonization shrink concretes. In such concrete projects not contacted with the atmosphere as the foundation works ,etc., because of isolating with CO2, can take plac
41、e carbonization react , so can mix and add the fly ash more , in order to fully reduce the heat of hydration of the concrete, improve the durability of the concrete. It is ultra to be adopt law quantity replace,water glue not lower than,mix carry on match ratio design water-reducing agent for admixt
42、ure of main fact at the same time, can make fly ash concrete resist carbonization performance improve to some extent.3.6 reinforcing bar corrosion Reinforcing bar of concrete can it antirusts to be because concrete getting alkaline to form one pre-pressing passivation membrane in metal surface. Is i
43、t add fly ash to mix among concrete, on one hand it consume Ca (OH ) 2, reduce the alkali environment of the concrete; On the other hand, fly ash 2 responses turn into the hyrate with Ca (OH), raise closely knit degree of the concrete, increase the impermeability of the concrete and obstruction spre
44、ad to the chlorine ion, hinder and prevent the invasion of CO2, can shield the reinforcing bar , so fly ash is mixed, in preventing the reinforcing bar corrosion, can offset because alkali degree reduce adverse effect that bring. The fly ash is on certain range (FA 24% ) of mixing amount, have not i
45、nfluenced the reinforcing bar corrosion basically, even superior to the blank concrete. But if the mixing amount of the fly ash is greater than 30%, the carbonization of the concrete can make hydrogen ion index of the concrete dropped to about 8.5 from 12.5 , under so low a hydrogen ion index condit
46、ion, the reinforcing bar is no longer passivated. Reach reinforcing bar position by depth as carbonization, complete carbonization , on terms that water and oxygen are permeated antiabrasion layer, reinforcing bar can take place but corrosion lead to the fact fracture of the concrete even destroy.3.
47、7 heat of hydration The fly ash is very obvious to reducing the function of the concrete heat of hydration. Low calcium fly ash water in the first several days obvious degree have, heat of hydration produced only and half of cement. Replace 20% of the cement with fly ash in the concrete , can make t
48、he heat of hydration of concrete 7d drop by 11% . 1-28d in the issue, roughly for mix percentage of fly ash, Sheng Wen and percentage that heat of hydration reduce age. Fly ash is it can make heat of hydration time that peak appear is it appear to 3d to delay generally to mix among large volume conc
49、rete, can prevent the concrete from producing the temperature crack effectively .粉煤灰高性能混凝土的工程应用摘要 本文对粉煤灰高性能混凝土的各项性能作了详细的研究，并针对粉煤灰的掺入量对混凝土各 种性能的影响以及粉煤灰混凝土在施工中应注意的一些问题进行了分析和探讨。 1概 述 粉煤灰作为一种工业废料，资源丰富、价格低廉，且含有大量的活性成分，是现代混凝土中非常重要的一个组分。优质粉煤灰合理地应用于混凝土中，不但能部分代替水泥，节省工程造价，而且，其特有的性能可以很有效地用于各种使用要求的混凝土中，改善和提高混凝土的性能，是高性能混凝土中的理想掺和料。在现代混凝土中，粉煤灰已经与水泥、集料、水、外加剂同样重要，成为混凝土中的一个组分。粉煤灰高性能混凝土是以耐久性为主要目标进行设计的混凝土。它以优异的耐久性（而不是高强度）为主要特征，也就是说，任何强度等级的混凝土都可以做成高耐久性混凝土。为达到高耐久性，粉煤灰混凝土应具备的性能是：在新拌状态有良的工作性，即高流动性而不离析、不泌水，以使成型均匀、密实，水化硬化早期的沉降收缩和水化收缩小，温升低，硬化过程干缩小，以达到无初始裂缝，硬化后的渗透性低。 2对“粉煤灰效应”的认识 粉煤灰的“功能”和“效应”是所有粉煤灰材料技术和工程的应