1、技 术 通 报类别案号 001206版本 0页次 1/2主题 常用金属材料及其规格背景 由于对金属材料认识太少,对工作造成困扰1. 一般红铜或高导红铜(Tough Pitch Copper)JIS H3100Alloy No. Hardness (T/Strength) CuC1100R-O HV60 (195N/mm min) 99.90%minC1100R-1/4H HV55-100 (215-275N/mm)C1100R-1/2H HV75-120 (245-315N/mm)C1100R-H HV80-up (275N/mm min)2. 黄铜或青铜(Brass Strips)JIS H
2、3100Alloy No. Hardness (T/Strength) Cu ZnC2680R-O HV70-up (275N/mm min) 64-68% BalanceC2680R-1/4H HV75-125 (325-410N/mm)C2680R-1/2H HV85-145 (355-440N/mm)C2680R-H HV105-175 (410-540N/mm)C2680R-EH HV145-up (520N/mm min)3. 磷青铜(Phosphor Bronze Strips)JIS H3110Alloy No. Hardness (T/Strength) SnC5191R-O
3、HV70-up (315N/mm min) 5.5-7.0%C5191R-1/4H HV100-160 (390-510N/mm)C5191R-1/2H HV150-205 (490-610N/mm)C5191R-H HV180-230 (590-685N/mm)C5191R-EH HV200-up (635N/mm min)4. 高质弹璜用磷青铜(High Quality Phosphor Bronze Spring Strips)JIS H3130Alloy No. Hardness (T/Strength) SnC5210R-1/2H HV140-205 (470-610N/mm) 7.
4、0-9.0%C5210R-H HV185-235 (590-705N/mm)C5210R-EH HV210-260 (685-785N/mm)C5210R-SH HV230-270 (735-835N/mm)结论发行对象 R/D 工模部 制造部 品保 资材 审核 制作人金洋五金 版本:A 窗体编号:JY-ENG-004技 术 通 报类别案号 001206版本 0页次 2/2主题 常用金属材料及其规格背景 由于对金属材料认识太少,对工作造成困扰5. 不锈钢带(Stainless Steel Strips)JIS G4313 “Spring Temper” (弹璜用)SUS 301 CSP 1/4
5、H HV270min1/2H HV310min (932N/mm min)3/4H HV370min (1128N/mm min)H HV430min (1324N/mm min)EH HV490min (1569N/mm min)SUS 304 CSP 1/4H HV210min1/2H HV250min (785N/mm min)3/4H HV310min (932N/mm min)H HV370min (1128N/mm min)JIS G4307 “Anmealed 生”SUS 304-2B/BA HV150-190 (608-745N/mm)(HRB78-89)成 份:C Ni Cr
6、SUS301 0.15max 6-8 16-18SUS304 0.08max 8-10.5 18-20SUS304L 0.03max 9-13 18-20用 语:2 B : 压延 热处理 压延BA : 压延 光辉处理2 D : 压延 热处理 洗酸HL : 研磨处理6. 中碳钢(C1050H/2 或 550C)调质热处理硬度 HRC3537方盒类产品7. 高碳钢: (SK5 SK7) 调质热处理,热处理后弹性增加,可以做弹片使用。注：热处理后,不可清洗,否则生锈8. 铁材(SPCC)螺帽类产品,无需热处理,直接电镀。结论发行对象 R/D 工模部 制造部 品保 资材 审核 制作人金洋五金 版本:A 窗体编号:JY-ENG-004