1、1EN71-3 2013 Safety of toys - Part 3: Migration of certain elements玩具安全-第 3 部分：元素的迁移1 Scope（范围）This European Standard specifies requirements and test methods for the migration of aluminium, antimony, arsenic, barium, boron, cadmium, chromium (III), chromium (VI), cobalt, copper, lead, manganese, mer
2、cury, nickel, selenium, strontium, tin, organic tin compounds and zinc from toy materials and from parts of toys.本欧洲标准规定了下列从玩具材料和玩具部件中转移的元素的详细要求和测试方法：铝、锑、砷、钡、硼、镉、铬（3+） 、铬（6+） 、钴、铜、铅、锰、汞、镍、硒、锶、锡、有机锡和锌。Packaging materials are not considered to be part of the toy unless they have intended play value.包装
3、材料不包括在本标准范围之类，除非它们属于玩具部分或者有娱乐价值。The standard contains requirements for the migration of certain elements from the following categories of toy materials: Category I : Dry, brittle, powder like or pliable materials; Category II : Liquid or sticky materials; Category III : Scraped-off materials.下列玩具种类的
4、元素转移包括在本标准的要求之内：第一类：干燥，易碎，粉末状或柔软的玩具材料；第二类：液体状/粘稠性玩具材料；第三类：玩具表面刮出物。The requirements of this standard do not apply to toys or parts of toys which, due to their accessibility,function, volume or mass, clearly exclude any hazard due to sucking, licking or swallowing or prolonged skin contact. Both the i
5、ntended and foreseeable use has to be considered, bearing in mind the behaviour of children,某些玩具和玩具零件，在考虑儿童正常的和可预见性的行为时，这些部分由于它们的可接触性、功能、质量、大小或其它的特性，可明显排除因吮吸、舔食2和吞咽造成的危害，这部分玩具不包括在EN 71标准的这一部分之内。NOTE 2 For the purposes of this standard, for the following toys and parts of toys the likelihood of sucki
6、ng, licking or swallowing toys is considered significant:All toys intended to be put in the mouth or to the mouth, cosmetics toys and writing instruments categorised as toys may be sucked, licked or swallowed; All the accessible parts and components of toys intended for children up to 6 years of age
7、 may come into contact with the mouth. The likelihood of mouth contact with parts of toys intended for older children is not considered significant in most cases; 备注2：为了执行本标准，下列标准适用于判断吮吸、舔食、吞咽的产品范围：所有供给食物或与嘴唇接触的玩具、化妆玩具和属玩具类的书写工具；供 6 岁及以上儿童使用的玩具，即所有可能与嘴接触到的部分或零件，对于大孩子来说，嘴与玩具部件的接触在大部分情况下被认为是不重要的。2 Nor
8、mative references（参考标准）EN 71-1:2011, Safety of toys Part 1: Mechanical and physical properties EN ISO 3696, Water for analytical laboratory use Specification and test methods (ISO 3696)EN 71-1:2011, 玩具的安全 第 1 部分: 物理机械性能 EN ISO 3696, 分析实验室用水 规格和测试方法(ISO 3696)3. Terms and definitions（术语和定义） （略）4. Requ
9、irements（要求）4.1 Toy categories（玩具的分类）Table 1 Cross-reference table for determining category（表1 玩具材料分类的参照表）Toy Material 玩具材料 Category I种类Category II种类Category III种类Coatings of paints, varnishes, lacquers, printing inks, polymers, foams and similar coatingsX3涂层：油漆、清漆、生漆、印刷油墨、聚合物、海绵和类似的涂层Polymeric and
10、similar materials, including laminates, whether textile reinforced or not, but excluding other textiles高分子材料和类似的材料，包括不论是否有纺织物增强的层压材料，但不包括其它的纺织物XPaper and paper board纸张和纸板XTextiles, whether natural or synthetic天然或合成纺织物XGlass, ceramic, metallic materials玻璃，陶瓷，金属材料XOther materials whether mass coloured
11、 or not (e.g. wood, fibre board, hard board, bone and leather)其它材料，不管是否被染色（例如：木材、纤维板、硬质板、骨头和皮革）XCompressed paint tablets, materials intended to leave a trace or similar materials in solid form appearing as such in the toy (e.g. the cores of colouring pencils, chalk, crayons)压缩漆，会留下痕迹的或类似的以固体形式出现在玩具上
12、的材料（例如：彩色铅笔芯，粉笔、蜡笔）XPliable modelling materials, including modelling clays and plaster软性造型材料，包括造型粘土和石膏X4Liquid paints, including finger paints, varnishes, lacquers, liquid ink in pens and similar materials in liquid form appearing as such in the toy (e.g. slimes, bubble solution)液体油漆，包括指画颜料、清漆、生漆、笔里
13、面的液体油墨和在玩具上呈液态的类似材料（例如煤泥、泡泡水）XGlue sticks 固体胶 X4.2 Specific requirements（特殊要求）The migration of elements from toy materials categorised in accordance with 4.1 shall not exceed the migration limits given in Table 2 when tested in accordance with Clauses 7 and 8. 根据4.1对玩具材料做出分类，根据条款7和8检测出来的元素的迁移值不得超过表2
14、给出的限值。Table 2 Migration limits from toy materials 表 2 玩具材料的迁移限量Element 元素 Category I种类(mg/kg)Category 种类(mg/kg)Category 种类(mg/kg)Aluminium 铝 5625 1406 70000Antimony 锑 45 11.3 560Arsenic 砷 3.8 0.9 47Barium 钡 1500 375 18750Boron 硼 1200 300 15000Cadmium 镉 1.3 0.3 17Chromium (III)铬（3+ ）37.5 9.4 460Chrom
15、ium (VI)铬（6+ ）0.02 0.005 0.2Cobalt 钴 10.5 2.6 130Copper 铜 622.5 156 77005Lead 铅 13.5 3.4 160Manganese 锰 1200 300 15000Mercury 汞 7.5 1.9 94Nickel 镍 75 18.8 930Selenium 硒 37.5 9.4 460Strontium 锶 4500 1125 56000Tin 锡 15000 3750 180000Organic tin 有机锡 0.9 0.2 12Zinc 锌 3750 938 460005 Principle（原理）Soluble
16、 elements are extracted from toy materials under the conditions which simulate the material remaining in contact with gastric simulant for a period of time after swallowing. The concentrations of the soluble elements are determined quantitatively by three different methods: Method for determining ge
17、neral elements: Aluminium, Antimony, Arsenic, Barium, Boron, Cadmium, Cobalt, Copper, Lead, Manganese, Mercury, Nickel, Selenium, Strontium, Tin and Zinc; Method for determining Chromium (III) and chromium (VI); Method for determining Organic tin. 模拟材料在吞咽后与胃酸持续接触一段时间，在此条件下，可溶性的元素被从玩具材料中萃取出来。根据三种不同的方
18、法对可溶性元素定量分析。标准元素(铝、锑、砷,钡,硼、镉、钴、铜、铅、锰、汞、镍、硒、锶、锡和锌);铬(III)和铬 (VI);有机锡。6 Reagents and apparatus（试剂和仪器）6.1 Reagents（试剂）All chemicals used for analysis shall be of analytical grade 66.1.1 Hydrochloric acid solution, c(HCl) = (0,07 0,005) mol/L 6.1.2 Hydrochloric acid solution, c(HCl) = (0,14 0,010) mol/L
19、 6.1.3 Hydrochloric acid solution, c(HCl) = approximately 1 mol/L 6.1.4 Hydrochloric acid solution, c(HCl) = approximately 2 mol/L 6.1.5 Hydrochloric acid solution, c(HCl) = approximately 6 mol/L 6.1.6 n-Heptane, (C7H16), 99% 6.1.7 Water, of at least grade 3 purity in accordance with EN ISO 3696.6.1
20、 试剂在分析中，只能使用经过认可的分析纯试剂。6.1.1 盐酸溶液，c （HCl ）=（0.070.005）mol/l6.1.2 盐酸溶液，c （HCl ）=（0.140.010）mol/l。6.1.3 盐酸溶液，c （HCl ）=约1mol/l。6.1.4 盐酸溶液，c （HCl ）=约2mol/l。6.1.5 盐酸溶液，c （HCl ）=约6mol/l。6.1.6 正庚烷（C 7H16）：99%。6.1.7 水：纯度至少达到ISO 3696 所规定的三级。6.2 ApparatusStandard laboratory equipment and the following shall b
21、e used. 6.2.1 Plain weave wire cloth stainless steel sieve, of nominal aperture size 0,5 mm 6.2.2 A means to measure the pH, with an accuracy of 0,2 pH units. 6.2.3 Centrifuge，capable of centrifuging at high speed to separate the solids. 6.2.4 A means to agitate the mixture, at a temperature of (37
22、2) C. 6.2.5A selection of containers of gross volume, between 1,6 times and 5,0 times that of the volume of hydrochloric acid extract.6.2.6 High retention filter-paper, ashless filter paper, particle retention in liquids 2.5m.6.2.7 Membrane filter, with a pore size of 0,45,0.22 and 0.02m6.2 仪器常规的实验仪
23、器有：76.2.1 平纹金属丝网不锈钢金属筛，筛网孔径大小为0.5mm6.2.2 测量pH 值的设备，准确到0.2 个pH 单位。6.2.3 离心机，能高速分离固体。6.2.4 搅拌混合物的装置，搅拌时温度为（372）。6.2.5 一套容器，总体积为盐酸萃取剂体积的 1.6-5.0 倍的容器。6.2.6 高效滤纸，无尘滤纸，在液体的粒子滞留为 2.5 m。6.2.7 滤膜过滤器，滤孔为0.45, 0.22和0.02m。7 Sampling and sample preparation（样品和样品制备）7.1 Selection of test portionsA laboratory samp
24、le for testing shall consist of one toy in the form in which it will be marketed. Test portions shall be taken from toy materials of the single toy sample. Identical materials in the toy may be combined and treated as a single test portion but additional toy samples shall not be used to prepare larg
25、er test portions. Test portions are taken from each colour of each toy material. Test portions may be composed of more than one toy material or colour only when discrete specimens cannot be separated physically, e.g. dot printing, patterned textiles etc. NOTE This requirement does not preclude the p
26、reparation of test portions which represent the material and any base material upon which it is deposited. If the total weight of accessible toy material available is less than 10 mg test portions need not be prepared.The above does not preclude the possibility of testing toy materials before they a
27、re used to manufacture a toy in order to prove compliance of the final toy. It must be assessed that the manufacturing process does not influence the migration of elements from the toy materials.7.1 测试部位的选择供测试的玩具样品应是销售状态的玩具，试样应从单个玩具样品上取下，即：单个玩具上同种材料可以结合起来作为同一测试试样，但不应采用其它玩具样品。测试试样不应含一种以上材料或一种以上颜色，除非采
28、用物理分离方法不能有效分离的样品，这种样品如点染色、印花纺织物或因重量限制的样品。8注：本要求不排除可以从能代表试样的材料及其附着的衬底材料上取下的测试试样。对材料不足10mg的测试部分不进行测试。以上不排除检测玩具材料的可能性，因为这些材料是用于制作玩具以证明符合最终玩具的要求。在这种情况下，它应该被评估在制造过程中不影响玩具材料中元素的迁移。7.2 Standards preparation（标准溶液的制备）Prepare standard solutions in a proper working range according to the required limits for ea
29、ch element for the three categories.在一个合适的工作范围内根据三类物质中每一种元素的限值准备标准溶液。7.3 Sample preparation（样品的制备）7.3.1 General A blank solution shall be determined for any bias. The analytical results shall be corrected for this bias. For example for any contaminants that may be present in the filter paper or the
30、gastric simulant.测定一个空白溶液，有任何偏差分析结果应该被校正。例如出现在滤纸上或者模拟液的污染物。7.3.2 Category I: Dry, brittle, powder like or pliable and Category II: Liquid or stickyIf possible obtain a test portion of not less than 100 mg of the material from the laboratory sample. If a test portion of 100 mg or more cannot be obtai
31、ned, a test portion shall be obtained from each toy material present in the laboratory sample in a mass greater than 10 mg. If the weight of the test portion obtained is between 10 mg and 100 mg, that weight shall be reported (see clause 10 h). In this case the analytical results shall be calculated
32、 as though 100 mg of the test portion had been used. If the toy material contains any grease, oil, wax or similar material, material shall be de- waxed. De - waxing shall not be carried out on test portions being analysed for organic tin. Dry a high retention filter paper for 4 hours at 37C. Weigh t
33、he filter paper to the nearest 0.1 mg (Wfp1). The filter paper used should be as small as possible without risking loss of the test portion during the de- waxing procedure. 9Weigh the test portion, to the nearest 0, 1 mg, onto the pre - dried and weighed filter paper. Fold the filter paper carefully
34、 to enclose the test portion without loss. Extract the test portion within the filter paper with boiling n - heptane using suitable laboratory apparatus. The use of a de- waxing step shall be reported (see clause 10 h). It has been shown that Soxhlet extraction with n-heptane for 6 hours is usually
35、sufficient to completely remove non-polar ingredients from waxy toy materials. Alternative methods should be validated to show that they are capable of completely removing the non-polar ingredients from relevant toy materials.After removal of non- polar ingredients, dry the folded filter paper conta
36、ining the dewaxed test portion in an oven at 37C 2 for 4 hours to ensure the removal of residual solvent. Weigh the dried filter paper parcel, to the nearest 0.1 mg (Wfp2). Use Wfp2 for the calculation under 7.4.2.1 on the volume of 0.07 M HCL.7.3.2 第一类：干燥，易碎，粉末状或柔软的玩具材料；第二类：液体或者粘性材料从实验室样品上取下不少于 100
37、mg 的测试材料。如果不能获得100mg或者100mg以上的测试材料，测试材料必须从每种不同玩具材料上获得大于 10mg 的质量。如果材料为10mg至100mg 之间，测试部分的质量必须注明（见条款10h），同时有关元素的含量必须按使用的测试试样为100mg 计算。如果玩具材料含有油脂、油类、蜡或类似材料，应执行去蜡程序。有机锡的测试样品不用执行去蜡测试。将高效滤纸在37烘4个小时。称取滤纸的重量，精确到0.1mg (Wfp1) 。为了在去蜡的过程中减少样品的损失，滤纸应尽可能的小。称量样品，精确到0.1mg。将测试试样包在高效滤纸中，使用沸腾的正庚烷去油脂直至完全清除。如果执行去油程序应注明
38、（见条款10h）。证明显示，用正庚烷进行6小时的索氏提取能彻底清除蜡质玩具材料的非极性成分。用其它方法验证表明他们有能力完全去除有关玩具材料的非极性成分。移去非极性物质后，含有油脂检测样品的折叠滤纸在372烘4个小时确保移除残留物质，称量干燥的滤纸包，精确到0.1 mg (Wfp2)。用Wfp2 计算7.4.2.1中HCL溶液的体积。7.4.3 Category III: Scraped-off（第三类：玩具表面刮出物） 。107.4.3.1 Coatings of paint, varnish, lacquer, printing ink, polymer and similar coati
39、ngs Remove the coating from the laboratory sample by mechanical means (usually scraping) at room temperature. If possible obtain a test portion of not less than 100 mg passing through a metal sieve of aperture 0,5 mm.If the weight of the test portion obtained is between 10 mg and 100 mg, that weight
40、 shall be reported (see clause 10 h). In this case the analytical results shall be calculated as though 100 mg of the test portion had been used. When possible coatings on textiles may be scraped off as a powder(and report this under clause 10 h). In case of a thick layer or one which is difficult t
41、o remove (e.g. pliable or plasticized layers), the coating can be cut off and tested as polymeric material (7.3.2.2).7.3.3.1 油墨、清漆、生漆、印刷墨水、聚合物涂层和类似的涂层在室温下采用机械方法（通常是刮）从试样上获取涂层。从能通过孔径为 0.5mm的金属筛网的筛分材料中获取不少于100mg 的测试试样。如果粉碎后的同一种涂层仅能得到 10mg 至100mg，测试部分的质量必须注明（见条款10h）。有关元素的含量应按使用的测试试样为100mg 计算。纺织品上的涂层可以作
42、为粉末刮下来（见条款10h）。如果涂层比较厚而且很难刮下来，则可以做为聚合物材料直接剪切下来（7.3.2.2）。7.3.3.2 Polymeric and similar materials including laminates and reinforced textiles, but excluding other textiles If possible obtain a test portion of not less than 100 mg of the polymeric or similar material, according to the following directi
43、ons. Cut out test portions from the areas having the thinnest material cross section. Each test piece shall have a maximum dimension of no more than approximately 6 mm. The use of pre-prepared reference materials for visual size comparison is recommended. If a test portion of 100 mg or more cannot b
44、e obtained, a test portion shall be obtained from each toy material present in the laboratory sample in a mass greater than 10 mg. If the weight of the test portion obtained is between 10 mg and 100 mg, that weight shall be reported (see clause 10 h). In this case the analytical results shall be cal
45、culated as though 100 mg of the test portion had been used.117.3.3.2 聚合物材料和类似材料，包括用或不用纺织物增强的层压材料，但不包括其它纺织物从聚合物或类似材料上取下不少于 100mg 的测试部分，具体方法如下：从材料截面厚度最小处剪下测试部分。每个试样的所有尺寸要小于6mm。视觉尺寸可以与事先准备好的材料相比较。如果不能获得100mg或者100mg以上的测试材料，测试材料必须从每种不同玩具材料上获得大于 10mg 的质量。如果材料为10mg至100mg 之间，测试部分的质量必须注明（见条款10 h），同时有关元素的含量必须
46、按使用的测试试样为100mg 计算。7.3.3.3 Paper and paper board If possible obtain a test portion of not less than 100 mg of the paper or paper board . Each test piece shall have a maximum dimension of no more than approximately 6mm. The use of pre-prepared reference materials for visual size comparison is recommen
47、ded. If a test portion of 100 mg or more cannot be obtained, a test portion shall be obtained from each toy material present in the laboratory sample in a mass greater than 10 mg. If the weight of the test portion obtained is between 10 mg and 100 mg, that weight shall be reported (see clause 10 h).
48、 In this case the analytical results shall be calculated as though 100 mg of the test portion had been used. If the paper or paper board to be tested is coated with a coating of paint, varnish, lacquer, printing ink, adhesive or similar coating, test portions of the coating shall not be taken separa
49、tely. In such cases test portions shall be taken from the toy material so that they also include representative parts of the coated area. 7.3.3.3 纸或纸板从纸或纸板上取下不少于 100mg 的测试部分。每个试样的所有尺寸在不受压的状态下必须小于6mm。视觉尺寸可以与事先准备好的参考材料相比较。如果不能获得100mg或者100mg以上的测试材料，测试材料必须从每种不同玩具材料上获得大于 10mg 的质量。如果材料为10mg至100mg 之间，测试部分的质量必须注明（见条款10h），同时有关元素的含量必须按使用的测试试样12为100mg 计算。如果待测试的纸或纸板上有油漆、清漆、生漆、油墨、胶粘剂涂层或类似涂层，涂层的测试试样不应分开移取。在这种情况下，测试试样从材料上直接取下，使测试试样同时包括含涂层部位的代表性试样。7.3.3.4 Textiles, whether natural or synthetic If possible obtain a test portion of not