1、Designation: A 358/A 358M 01 An American National Standard 名称:A358/A358M-01 Used in USDOE-NE Standards美国国家标准用于 USDOE_NE 标准Standard Specification for Electric-Fusion-Welded Austenitic Chromium-Nickel Alloy Steel Pipe for High-Temperature Service1 高温用电熔焊奥氏体铬镍合金钢管标准规范This standard is issued under the f
2、ixed designation A 358/A 358M; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (e) indicates an editorial change since
3、 the last revision or reapproval. 此标准以固定名称 A358/ A 358 M 发布, 紧随名称之后的数字，表示采用本标准的年份或上次修改本标准的年份。上方的希腊字母(e)表示上一次再版或审核的版次变化。1. Scope 范围1.1 This specification2 covers electric-fusion-welded austenitic chromium-nickel alloy steel pipe suitable for corrosive or high-temperature service, or both. 此规范适用于腐蚀环境或
4、高温环境的电熔焊奥氏体铬镍合金钢管。NOTE 1The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter,” “size,” and “nominal size.” 注 1- 无量纲符号 NPS（名义钢管尺寸）在此标准中替换为传统的术语“名义直径” “尺寸”和“标称尺寸”1.2 This specification covers nineteen grades of alloy
5、 steel as indicated in Table 1. The selection of the proper alloy and requirements for heat treatment shall be at the discretion of the purchaser, dependent on the service conditions to be encountered.此规范包含图表 1 中 19 个级别的合金钢。根据使用条件，买方应慎重选择合适的合金钢，和正确的热处理程序。1.3 Five classes of pipe are covered as follo
6、ws:下列包括 5 种类别的钢管 1.3.1 Class 1Pipe shall be double welded by processes employing filler metal in all passes and shall be completely radiographed. 1 类 钢管采用所有焊道填充金属的双面焊，并完全经过射线检查。1.3.2 Class 2Pipe shall be double welded by processes employing filler metal in all passes. No radiography is required. 2 类
7、 钢管采用所有焊道填充金属的双面焊，不需要射线检查。1.3.3 Class 3Pipe shall be single welded by processes employing filler metal in all passes and shall be completely radiographed. 3 类 钢管采用所有焊道填充金属单面焊，并完全经过射线检查。1.3.4 Class 4Same as Class 3 except that the weld pass exposed to the inside pipe surface may be made without the a
8、ddition of filler metal (see 6.2.2.1 and 6.2.2.2).4 类 和三类相同，只是焊道暴露于钢管内壁，可能没有填加填充金属。 1.3.5 Class 5Pipe shall be double welded by processes employing filler metal in all passes and shall be spot radiographed.5 类 钢管采用所有焊道金属填充的双面焊，应进行缺陷射线检测 1.4 Supplementary requirements covering provisions ranging from
9、 additional testing to formalized procedures for manufacturing practice are provided. Supplementary Requirements S1 through S6 are included as options to be specified when desired.提供了补充要求，包括附加测试到生产实践的正规程序等条款。作为详细说明的选项，补充说明 S1-S6 也包括在内。1.5 The values stated in either inch-pound units or SI units are
10、to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specific
11、ation. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order. 本文中所述的值或以英寸磅为单位，或采用国际单位，应作为标准区分对待。在本文中，国际单位在括号内表示。各系统所表示的数值不完全相等，所以每一系统必须区别于另一系统单独使用。两个系统的数值混在一起使用会导致规范的不一致。应采用英寸磅单位，除非在顺序上指定 M 为首选。2. Referenced Documents参考资料 2.1 ASTM Standards: ASTM
12、 标准。A 240/A 240M Specification for Heat-Resisting Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels 注 3 A240/A 240M 压力容器用耐热铬及铬镍不锈钢板，薄板和带材A 262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels注 3 A262 奥氏体不锈钢晶间浸蚀敏感度检测
13、的应用A 480/A 480M Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip3 A480、A480M 平面轧辊不锈钢和耐热钢板材、薄板和带材一般要求的标准规范A 941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys4 A941 钢，不锈钢,相关合金和铁合金术语A 999/A 999M Specifica
14、tion for General Requirements for Alloy and Stainless Steel Pipe 4 A999/A999M 合金和不锈钢管的一般要求规范。E 527 Practice for Numbering Metals and Alloys (UNS)4 E527 金属及合金编号（统一编号系统）2.2 ASME Boiler and Pressure Vessel Code: Section I, Welding and Brazing Qualifications5 Section IX, Welding Qualifications5 ASME 锅炉和
15、压力容器准则2.3 AWS Specifications:6 美国焊接学会规范A 5.22 Flux Cored Arc Welding 管状焊丝电弧焊A 5.30 Consumable Weld Inserts for Gas Tungsten Arc Welding钨极气体电弧焊A 5.4 Corrosion-Resisting Chromium and Chromium-Nickel Steel Covered Welding Electrodes 耐腐蚀铬及铬镍钢覆盖焊条A 5.9 Corrosion-Resisting Chromium and Chromium-Nickel Ste
16、el Welding Rods and Bare Electrodes 耐腐蚀铬及铬镍钢焊条和裸焊条A 5.11 Nickel and Nickel-Alloy Covered Welding Electrodes 镍和镍合金包裹焊条A 5.14 Nickel and Nickel-Alloy Bare Welding Rods and Electrodes 镍和镍合金裸焊条2.4 Other Standard: 其它标准注：1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainl
17、ess Steel, and Related Alloys, and is the direct responsibility of Subcommittee A01.10 on Stainless and Alloy Steel Tubular Products. 此规范归属于钢，不锈钢及相关合金 ASTM A01 委员会，不锈钢以及合金钢管材产品则归属于 A01.10 小组委员会。Current edition approved Mar. 10, 2001. Published May 2001. Originally published as A 358 52 T. Last previ
18、ous edition A 358/A 358M 00. 当前版本核准于 2001 年 3 月 10 日。2001 年 5 月发行。原版本为 A358-52T。此前最后一次版本为 A358 A358M-002 For ASME Boiler and Pressure Vessel Code applications see related Specifications SA-358 in Section II of that Code. 对于 ASME 锅炉和压力容器准则的应用请见相关规范。3 Annual Book of ASTM Standards, Vol 01.03. ASTM 标准年
19、刊，01,03 卷4 Annual Book of ASTM Standards, Vol 01.01. ASTM 标准年刊，01,01 卷5 Available from ASME International, Three Park Avenue, New York, NY 100165990. 纽约三公园大道 ASME 国际 10016-5990 有售。6 American Welding Society, 550 LeJeune Road, P.O. Box 351040, Miami, FL 33135. 美国焊接学会，佛罗里达州，迈阿密，Lejeune 路 550 号，351040
20、信箱Copyright . ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States. 著作权 美国，巴拿马州，西康舍霍肯，港口大道 100 号， 电话 19428-2959COPYRIGHT American Society for Testing and Materials Licensed by Information Handling Services 著作权 美国材料与试验协会信息处理部许可。原件第一页结束TABLE 1 Plate and Filler Metal Specificati
21、ons 表格 1 板材和填充金属规范 图详见原图图下注释：A New designation established in accordance with ASTM E 527 and SAE J 1086. 新的名称根据 ASTM527 和 SAE 标准建立。B Choice of American Welding Society specification depends on the welding process used. 选择美国焊接学会的规范应根据使用的焊接工艺。C In previous editions, S30600 was incorrectly shown as S01
22、815. 在之前版本，被错误的显示为SAE J1086 Practice for Numbering Metals and Alloys (UNS) 注 7 AEJ 1086 金属和合金编号的应用（统一编号系统） 。3. Terminology 术语3.1 Definitions: 定义3.1.1 The definitions in Specification A 999/A 999M and Terminology A 941 are applicable to this specification.A999 和 A999M 规范中的定义可以应用于此规范。4. Ordering Infor
23、mation 订货信息4.1 Orders for material under this specification should include the following, as required, to describe the desired material adequately: 在此规范下订购材料应按要求包含如下信息以充分描述所需材料。4.1.1 Quantity (feet, metres, or number of lengths),数量（英尺，米，或者长度的数量）注释7 Available from Society of Automotive Engineers, 400
24、 Commonwealth Drive, Warrendale, PA 15096. 巴拿马州，沃伦达市，共富大道 400 号，邮编 15096，汽车工程师协会有售原件第二页结束4.1.2 Name of material (electric-fusion-welded pipe),原材料名（电熔焊钢管） 4.1.3 Grade (Table 1), 级别（表格 1）4.1.4 Class (see 1.3), 级别（见 1.3）4.1.5 Size (outside diameter and nominal wall thickness),（尺寸，外直径和名义壁厚） 4.1.6 Length
25、 (specific or random), 长度 （指定或随机）4.1.7 End finish (Section on Ends of Specification A 999/ A 999M),管端的样式（A999/A999M 规范中管端的切面）4.1.8 Authorization for repair of plate defects by welding and subsequent heat treatment without prior approval if such is intended (see 9.3), 焊接缺陷修补的授权和在没有被许可的情况下相应的热处理（见 9.3
26、 部分）4.1.9 Specification designation, 规范名称4.1.10 Special requirements, 特殊要求4.1.11 Statement invoking requirements of 16.4 if such is intended. 16.4 部分需要陈述的要求。4.1.12 Circumferential weld permissibility (see Section 16), 圆周焊接的接受度（见 16 部分） 。4.1.13 Supplementary Requirements (S1 through S6), 补充要求（S1S6 ）4
27、.1.14 Applicable ASME Code if known, 可应用的已知的 ASME 标准4.1.15 For ASME Code Section III applications, the service classification intended, and对于 ASME 标准第三部分的应用，服务分类，4.1.16 Certification requirements (see Section on Certification of Specification A 999/A 999M). 认证要求（见 A999 和 A999M 规范中关于认证的部分）5. General
28、Requirements一般要求5.1 Material furnished to this specification shall conform to the applicable requirements of the current edition of Specification A 999/A 999M unless otherwise provided herein. 在此规范下供应的的材料应与当前版本的 A999 和 A999M 规范适用的要求一致，除非在此另外提供要求。6. Materials and Manufacture 材料和生产6.1 Materials: 材料6.1
29、.1 The steel plate material shall conform to the requirements of one of the grades of Specification A 240/A 240M, listed in Table 1, except as provided in 6.3.2.3. 钢板材料应与表格 1 中所列的 A240/A240M 规范中的某一级别的要求一致，6.3.2.3 所述状况除外。6.2 Welding: 焊接6.2.1 The joints shall be full penetration double-welded or singl
30、e-welded butt joints employing fusion welding processes as defined under “Definitions,” ASME Boiler and Pressure Vessel Code, Section IX. This specification makes no provision for any difference in weld quality requirements regardless of the weld joint type employed (single or double) in making the
31、weld. Where backing rings or strips are employed, the ring or strip material shall be of the same P-Number (Table QW-422 of Section IX) as the plate being joined. Backing rings or strips shall be completely removed after welding, prior to any required radiography, and the exposed weld surface shall
32、be examined visually for conformance to the requirements of 6.2.3. Welds made by procedures employing backing strips or rings which remain in place are prohibited. Welding procedures, and welding operators shall be qualified in accordance with ASME Boiler and Pressure Vessel Code, Section IX. 如 ASME
33、 锅炉和压力容器准则的定义中所述，焊缝为采用氧炔焊工艺焊透的双面焊或者单面对接焊。此规范并未就提出焊接质量方面的差异，无论在焊接中采用哪种焊缝类型（单面或者双面） 。焊接时，当使用条型衬垫后者环形衬垫时，所用材料应与产品号（P number） （第 9 章表格 QW-422）一致。在作任何射线检测之前，应在焊接完成后完全去除环形衬垫或条型衬垫，并应用肉眼检测裸露的焊接表面是否与 6.2.3 中要求一致。禁止采用条形衬垫或环形衬垫并保留在原位置。焊接程序和焊工都应具有符合第九章 ASME 锅炉和压力容器准则的资质。6.2.2 Except as provided in 6.2.2.1 and 6
34、.2.2.2, welds shall be made in their entirety by processes involving the deposition of filler metal. 除了 6.2.2.1 和 6.2.2.2 的情形，在保证填充金属沉淀过程的整体性。6.2.2.1 For Class 4 pipe employing multiple passes, the root-pass may be without the addition of filler metal. 对于 4 类管采用多道焊道，根部焊道可以不必添加金属。6.2.2.2 For Class 4
35、pipe, the weld surface exposed inside the pipe may result from a single pass made from the inside of the pipe without the addition of filler metal. 对于 4 类管，裸露在内的焊接表面可能由管道内部一个焊道引起，并未增加填充材料。6.2.2.3 All single-welded pipe shall be completely radiographed. 所有的单面焊管应进行完整的射线检测。6.2.3 The weld surface on eit
36、her side of the weld may be flush with the base plate or may have a reasonably uniform crown, not to exceed 1.8 in. 3 mm. Any weld reinforcement may be removed at the manufacturers option or by agreement between the manufacturer and purchaser. The contour of the reinforcement should be reasonably sm
37、ooth and free from irregularities. The deposited metal shall be fused uniformly into the plate surface. No concavity of contour is permitted unless the resulting thickness of weld metal is equal to or greater than the minimum thickness of the adjacent base metal. 焊接的任意一面的表面可能会与底盘一起变红或者产生合理的变形，不超过 1/
38、8 英寸（3mm） 。任何焊接补强都应按生产商的选择去除或者生产商和采购商达成一致。补强的外廓应平整，规则。堆积的金属应一致的熔入钢板表面。不允许轮廓有凹陷，除非导致的厚度等于或大于附近的底层金属的最小厚度。6.2.4 Weld defects shall be repaired by removal to sound metal and rewelding. Subsequent heat treatment and examination (that is, visual, radiographic, and dye penetrant) shall be as required on t
39、he original welds. 6.2.4 焊接缺陷应通过去除缺陷部分直至漏出金属并重新焊接的方法修补。应以原焊接同样的要求进行随后的检测（即 目测，射线检测和着色渗透检测） 。6.3 Heat Treatment: 热处理6.3.1 Unless otherwise stated in the order, heat-treatment shall consist of heating the material to a minimum temperature of 1900F 1040C except for S31266, S31254, S32654, S32050, and S
40、30815 which shall be heated to a minimum temperature of 2100F 1150C, and 1920F 1050C respectively, S24565 which shall be heated to a minimum temperature of 2050F 1120C, N08367 which shall be heated to a minimum temperature of 2025F 1107C, and N08926 which shall be heat treated to a minimum temperatu
41、re of 2010F 1100C, all treatments being followed by quenching in water or rapidly cooling by other means. N08904 shall be heat treated to a minimum temperature of 2000F 1095C and cooled rapidly. UNS N08810 shall be heated to a minimum temperature of 2050F 1120C and cooled rapidly. UNS N08020 shall b
42、e heated in the range from 1800 to 1850F 982 to 1010C and cooled rapidly.除非订单中另有陈述，否则热处理应包括把材料加热到至少 1900 华氏度（1040 摄氏度） ，S31266，S31254, S32654, S32050, 和 S30815 除外，应分别加热到至少 2100 华氏度（1150摄氏度）和 1920 华氏度（1050 摄氏度） ，S24565 应加热到至少 2050 华氏度（1120 摄氏度），N08367 应加热到至少 2025 华氏度（1107 摄氏度） ，N08926 应加热到至少 2010 华氏度
43、（1100 摄氏度） 。所有热处理后应淬火或采取其他方式急冷。N08904 应加热到至少 2000华氏度（1095 摄氏度）并急冷。 应加热到至少华氏度（摄氏度）并急冷。 应加热到华氏度（摄氏度）并急冷。6.3.2 The purchase order shall specify one of the following conditions if the heat-treated condition specified in 6.3.1 is not desired by the purchaser: 如果采购商并不需要规定的热处理条件，采购订单应规定如下条件之一。6.3.2.1 A fin
44、al heat-treatment temperature under 1900F 1040CEach pipe supplied under this requirement shall be Stenciled with the final heat-treatment temperature in degrees Fahrenheit or degrees Celsius after the suffix “HT”. Controlled structural or special service characteristics may be specified as a guide f
45、or the most suitable heat treatment. 在华氏度（摄氏度）以下最终热处理，在此要求下供应的每一根管应用字母后加最终热处理温度，采用华氏度或摄氏度，标记在管体。可以指定受控的结构性的或特别的服务特性作为最适合的热处理温度指南。6.3.2.2 No final heat treatment of pipe fabricated of plate that has been solution heat treated at temperatures required by this specificationEach pipe supplied under this
46、 requirement shall be stenciled with the suffix “HTO”. 无最终热处理的钢管，这种钢管的钢板材料经过本规范所要求的温度的溶液热处理，在此条件下供应的每一根管应在管体上标注字母 HT-O。6.3.2.3 No final heat treatment of pipe fabricated of plate that has not been solution heat treatedEach pipe supplied under this requirement shall be stenciled with the suffix “HT-S
47、O”.无最终热处理的钢管，这种钢管的钢板材料没有经过溶解热处理，在此条件下生产的每一根管应在管体上标注字母 HT-SO6.4 A solution annealing temperature above 1950F 1065C may impair the resistance to intergranular corrosion after subsequent exposure to sensitizing conditions in Grades 321, 347, and 348. When specified by the purchaser, a lower temperature
48、 stabilization or re-solution anneal shall be used subsequent to the initial high temperature solution anneal (see Supplementary Requirement S5). 321,347 和 348 级的溶液退火温度在 1950 华氏度（1065 摄氏度）可能在随后暴露于敏感条件中时削弱抗晶间腐蚀的耐受力。当采购商要求时，在先期高温溶液退火之后，应采用稍低温度的稳定或再溶解退火。7. Chemical Composition 化学构成7.1 The chemical comp
49、osition of the plate shall conform to the requirements of the applicable specification and grade 3 listed in Specification A 240/A 240M.钢板的化学构成应符合适用的规范的要求和 A240/A240M 规范中所列的 3 级的标准。原件第三页结束7.2 The chemical composition of the welding filler metal shall conform to the requirements of the applicable AWS specification for the corresponding grade shown in Table 1, or shall conform to the chemical composition specified for the plate in Sp